Annexes
Tableau 10 : Essai de
caractérisation des éprouvettes de l'ensemble supérieur
(S2)
|
Population d'éprouvettes
|
0%
|
6%
|
8%
|
10%
|
12%
|
|
Masse après confection Mh (g)
|
117.919
|
110.539
|
102.410
|
112,320
|
117,084
|
128,433
|
129.069
|
120,048
|
116,386
|
135,308
|
109.472
|
112.813
|
112.514
|
101.905
|
115.624
|
|
Masse après 28 j Ms (g)
|
91.199
|
99,427
|
94.893
|
110,942
|
109,020
|
122,046
|
116,052
|
112,426
|
108,521
|
112,118
|
94.851
|
108.314
|
106.078
|
95.401
|
105.740
|
|
Masse après 28 j à 105°C M's
(g)
|
-
|
-
|
-
|
83.750
|
98,400
|
108.670
|
112,381
|
102.814
|
96.547
|
124.854
|
101.021
|
103.104
|
97.901
|
84.846
|
96.673
|
|
Masse (M's) immergé dans l'eau M'h (g)
|
-
|
-
|
-
|
100.010
|
116,480
|
130,604
|
129.183
|
124.222
|
115.942
|
133.372
|
119.339
|
122.415
|
113.460
|
100,336
|
112.810
|
|
Longueur après fabrication L (mm)
|
80,200
|
80.300
|
80.200
|
80.200
|
80,200
|
80.200
|
80.200
|
80.500
|
80.200
|
80.200
|
80.200
|
80.200
|
80.300
|
80.300
|
80.400
|
|
Largeur après fabrication l (mm)
|
42.100
|
42.200
|
42.000
|
42,200
|
42.400
|
41.900
|
42.000
|
42.000
|
41.900
|
42.000
|
42.000
|
42,900
|
42.100
|
41.900
|
42.000
|
|
Epaisseur après fabrication h (mm)
|
18.100
|
17.100
|
16.500
|
17,800
|
17.300
|
19.500
|
19.500
|
18.000
|
17.700
|
19.500
|
15.800
|
18.700
|
17.000
|
15.300
|
16.800
|
|
Longueur après 28j
|
L0 (mm)
|
79,500
|
79,500
|
79.600
|
79,900
|
80.000
|
80.100
|
79,900
|
80.400
|
80.000
|
79,100
|
80.300
|
80.300
|
80.300
|
80.100
|
80.500
|
|
L1 (mm)
|
80.200
|
80.000
|
-
|
78,900
|
80.400
|
-
|
78,700
|
80.500
|
-
|
80.100
|
80.300
|
-
|
80.500
|
80.300
|
-
|
|
L2 (mm)
|
-
|
-
|
-
|
80.000
|
80.000
|
-
|
80,500
|
80.600
|
-
|
80.100
|
80.500
|
-
|
80.400
|
80.500
|
-
|
|
Largeur après 28 j
|
l 0 (mm)
|
41.800
|
41.800
|
41.800
|
41.800
|
41.900
|
42.000
|
41.800
|
42.000
|
41.900
|
41.900
|
42.000
|
42.000
|
42.000
|
41.700
|
42.000
|
|
l1(mm)
|
41.900
|
41.900
|
17.200
|
42.200
|
42.100
|
-
|
40.200
|
42.100
|
-
|
41,900
|
41.900
|
-
|
42.100
|
42.000
|
-
|
|
l2(mm)
|
-
|
-
|
16.200
|
41.700
|
41.800
|
-
|
42.900
|
42.200
|
-
|
41.900
|
42.200
|
-
|
41.800
|
42.100
|
-
|
|
Epaisseur après 28j
|
ho (mm)
|
17.500
|
19.000
|
17.000
|
-
|
17.400
|
17.800
|
-
|
16.500
|
17.900
|
-
|
17.000
|
17,000
|
-
|
17.500
|
16.600
|
|
h1(mm)
|
16.000
|
17.000
|
-
|
17, ;500
|
17.300
|
19.400
|
19.300
|
17.900
|
17.500
|
17.000
|
15.100
|
18.000
|
16.900
|
15.200
|
16.700
|
|
Force de flexion Ff (KN)
|
-
|
17.000
|
-
|
-
|
149.500
|
192.300
|
-
|
128.200
|
213.600
|
-
|
192,300
|
188,500
|
-
|
252.100
|
260,.500
|
|
Force de compression (KN)
|
Sèche Fcs
|
24.000
|
24.000
|
-
|
39,000
|
34,000
|
-
|
41,000
|
38,000
|
-
|
52,000
|
42,000
|
46,000
|
59,000
|
58,000
|
46,000
|
|
Humide Fch
|
-
|
-
|
-
|
28,220
|
17,000
|
-
|
21,000
|
30,000
|
-
|
27,000
|
37,000
|
-
|
35,000
|
38,000
|
-
|
|
Résistance à la flexion (Mpa)
óf
|
0,580
|
0.450
|
0,410
|
-
|
1.230
|
1.510
|
-
|
1,170
|
1.670
|
-
|
1,650
|
1,620
|
-
|
2.070
|
2.630
|
|
Résistance à la compression
(Mpa)
|
Sèche ócs
|
7.160
|
4.170
|
-
|
12,480
|
10.340
|
-
|
13.210
|
15,170
|
-
|
15,750
|
13.800
|
-
|
17,590
|
17,090
|
-
|
|
Humide óch
|
-
|
-
|
-
|
6,390
|
5.080
|
-
|
5.680
|
8.820
|
-
|
7.740
|
10.940
|
-
|
10,570
|
11.370
|
-
|
|
Retrait linéaire (%) R
|
+0,880
|
+0.100
|
+0,750
|
+0.370
|
+0.250
|
+0.120
|
+0.500
|
+0.120
|
+0.250
|
+0,240
|
+0.120
|
+0.120
|
+0.120
|
+0.240
|
+0.120
|
|
Coefficient d'absorption d'eau (%) ABS
|
-
|
-
|
-
|
19.400
|
18,320
|
20,480
|
19,690
|
17.930
|
20.080
|
18,400
|
18.130
|
18.720
|
18,900
|
18.250
|
16.690
|
|
Densité apparente
|
Humide ãh
|
1.930
|
1.910
|
-
|
1.980
|
1.990
|
1.960
|
1.980
|
1.980
|
1.940
|
2.060
|
2.060
|
1.790
|
1.960
|
1.980
|
2.040
|
|
Sèche ãs
|
1.730
|
1.760
|
-
|
1.880
|
1.880
|
1.870
|
1.800
|
1.870
|
1.850
|
1.970
|
1.850
|
1.780
|
1.860
|
1.860
|
1.860
|
LV
Mém. DEA-Sci. Géotechniques et Hydrotechniques
2003-2004
|
|